摘要本文论述了高强铝合金中厚板双脉冲熔化焊接工艺试验研究，铝合金焊接常见的问题，双脉冲MIG焊接对于单脉冲MIG焊接的优点及接头力学性能测试，了解高强铝合金焊接在国内外的现阶段研究状况及先进的技术手段。68188

本课题试验针对60mm厚的5A06铝合金板，应用双脉冲MIG焊接工艺，先在8mm的试板上进行堆焊，选取合适焊接工艺参数，进行多层多道对接焊接试验研究，并对获得的焊缝进行了宏观成型观察和微观组织分析。通过微观组织分析各种缺陷成因，提出合理的焊接工艺参数。

毕业论文关键词 5A06铝合金  双脉冲MIG  焊接工艺参数  多层多道焊  微观组织

毕业设计说明书（论文）外文摘要

Title   The Research on double-pulse welding process technology of

   high-strength thick aluminum-magnesium alloy        

Abstract： This paper discusses the double-pulse high strength aluminum alloy plate fusion welding process testing, aluminum welding common problem, double pulse MIG welding for single pulse MIG welding advantages and joints mechanical testing. Then we search and understand the study condition and advanced techniques of high-strength thick aluminum alloy welding now.

The main project is for the 60mm thick 5A06 aluminum alloy plate. The first trial in 8mm board use double pulse MIG welding process,for surfacing, from which select the appropriate welding parameters for butt welding test. Then we observe and analysis microscopic tissue of molding. By analyzing various microstructural defects we put forward a reasonable welding parameters.

Keywords  5A06 aluminum alloy  double pulse MIG  welding process parameters multipass welding  microstructure 

目  录

1  绪论 1

1.1 选题背景与选题意义 1

1.2 铝合金焊接技术现状 2

1.3 几种新型的铝合金焊接方法 4

1.3.1 搅拌摩擦焊 4

1.3.2 激光- 电弧焊 5

1.4 课题研究内容 6

2  试验材料和设备 7

2.1 试验材料 7

2.2 试验设备 7

2.3 焊接试验流程 8

2.3.1 焊前处理 8

2.3.2 施焊 9

2.4 金相组织分析 10

3  高强铝镁合金焊接工艺试验研究 12

3.1 堆焊焊接工艺研究 12

3.1.1 堆焊焊接规范 12

3.1.2 堆焊焊缝外观成型 12

3.2  对焊焊接工艺研究 14

3.2.1 坡口设计 14

3.2.2 多层多道焊接顺序规划 14

3.2.3 多层多道对接工艺试验 16

4　焊缝接头微观组织分析 24

4.1  焊缝微观组织分析 24

4.1.1  焊缝区微观组织 24

4.1.2  熔合区微观组织 25

4.1.3  热影响区微观组织 高强铝合金中厚板双脉冲熔化焊接工艺试验研究:http://www.751com.cn/cailiao/lunwen_76640.html