Ⅰ     Ⅱ     Ⅲ    平均值
                     10            111.3  108.3   109.1   109.6
                     15            119.5  119.5   116.9   118.6
   300℃             20            127.5  123.7   124.7   125.3
                     25            141.4  135.5   133.0   136.6
                     10            87.6   88.7    84.4    86.9
                     15            103.2  103.3   103.5   103.3
   350℃             20            115.4  113.5   112.2   113.7
                     25            118.0  123.0   121.4   120.8
                     10            87.2   81.2    79.7    82.7
                     15            92.6   92.1    88.3    91.0
   400℃             20            94.2   93.0    92.4    93.2
                     25            97.9   92.2    96.7    95.6
                     10            78.2   79.7    78.2    78.7
                     15            82.4   79.1    85.4    82.3
   450℃             20            88.6   83.1    82.1    84.6
                     25            85.3   85.7    87.9    86.3 2024铝合金冷塑性变形和再结晶退火的研究(6):http://www.751com.cn/cailiao/lunwen_1077.html