摘  要：以甲基丙烯酸为单体，N，N’-亚甲基双丙烯酰胺作为交联剂，过硫酸钾作为引发剂，自由基引发聚合制备聚甲基丙烯酸水凝胶。本论文研究了聚甲基丙烯酸水凝胶的溶胀率、平衡溶胀率，讨论了交联剂、引发剂的用量以及pH、盐溶液浓度对聚甲基丙烯酸水凝胶溶胀性能的影响。实验结果表明：当合成温度为80℃时，pH = 8，盐溶液浓度为0，交联剂、引发剂用量分别为反应物质量的0.6％、1.0％，所制备的水凝胶溶胀性能最好。10809
  关键词：聚甲基丙烯酸；水凝胶；平衡溶胀率；溶胀性能
Study on the Preparation of PMAA Hydrogel System
Abstract: Using Methacrylic acid as monosome, N, N'-methylene bisacrylamide as crosslinker, potassium persulfate as an initiator, the poly methyl methacrylate hydrogel was composed by the reaction of radical polymerization.The swelling ratio and water retention of poly methyl methacrylate hydrogel was researched, even, not only the amount of crosslinking and initiator but also the performance impact by the factors of pH and salt concentration was dissused.The experimental results show that: the swelling properties of the preparative hydrogel was best in the condition of the sintering temperature was 70 ℃, pH = 8, the concentration of the salt was 0, the amount of crosslinker and initiator was 0.6%, 1.0% of reactants.
Key Words: Polymethyl methacrylate; Hydrogels; Equilibrium; Swelling properties
目   　录
摘  要    1
引  言    1
1 实验部分    2
1.1 仪器与试剂    2
1.2 聚甲基丙烯酸水凝胶的制备    2
1.3 聚甲基丙烯酸水凝胶的纯化    3
1.4 聚甲基丙烯酸水凝胶的溶胀率测定    3
1.5 聚甲基丙烯酸水凝胶的平衡溶胀率测定    3
2 结果与讨论    3
2.1 聚甲基丙烯酸水凝胶溶胀动力学    3
2.2 聚甲基丙烯酸水凝胶受交联剂量影响的研究    4
2.3 聚甲基丙烯酸水凝胶受引发剂量影响的研究    5
2.4 聚甲基丙烯酸水凝胶受盐溶液浓度影响的研究    5
2.5 聚甲基丙烯酸水凝胶PH敏感性研究    6
3 结  论    7
参考文献    7
致  谢    10
聚甲基丙烯酸水凝胶的制备研究引 言   
水凝胶是一种新型的功能高分子材料，具有三文网络结构的适度交联的，不溶于水，但在水中膨胀吸收大量的水，并有很强的保水能力。水凝胶[1]可被定义为肿胀和保持在水的大量水分，和不溶性的交联聚合物。根据水凝胶相对于外界环境的改变性质是否发生变化，分为传统水凝胶与智能水凝胶。传统水凝胶对于外界环境的改变刺激不敏感，智能水凝胶却表现在对pH、光、温度、压力电场、离子强度、溶剂组成等外界环境反应敏感。
由于水凝胶材料含水量高，柔软，具有橡胶般的粘稠性和良好的生物相容性被广泛应用于生活的各个方面如工业，农林园艺，纺织，人工器官，医药医疗，生理卫生，石油化工，建材，环保，化妆品，食品，日用品等。在环境保护方面，利用高吸水性制成保水剂，可用于沙漠治理、土壤改良、水土保持等方面。在生物医学领域，可用作烧伤外涂敷物、药物传输体系、生物分子和细胞的固定化载体等。水凝胶带来了巨大经济效益和社会效益，因此各个国家对水凝胶的研究，开发，应用和生产呈现一派欣欣向荣的景象。水凝胶的研究和开发的相关学科如医药，水和土壤科学，生物技术，生命科学也随之发展。 聚甲基丙烯酸水凝胶的制备研究:http://www.751com.cn/huaxue/lunwen_9979.html