摘要本文报告了一种液相高度均匀和单分散的纳米氧化亚铜晶体的方法。在表面活性剂和有机物分子添加剂的存在下，在空气中分别用抗坏血酸和肼还原水中的铜（II）盐。随着表面活性剂和有机物分子添加剂浓度不断的变化，纳米氧化亚铜的尺寸从600nm变化到1000nm。对所有的样品进行扫描电子显微镜的表征，结果表明氧化亚铜样品的纳米颗粒呈比较规整的球形形状，且尺寸大小较为均匀，分散性好。70698
毕业论文关键字：液相合成，纳米氧化亚铜，有机物添加剂
Preparation and Properties of Regularized Morphology of Cuprous
Abstract This paper reports a method of highly uniform and monodispersed nanometer cuprous oxide crystals in liquid phase. The copper (II) salt in the water is reduced with ascorbic acid and hydrazine in air in the presence of a surfactant and an organic molecular additive. As the concentration of surfactants and organic molecules increases, the size of nanosized cuprous oxide varies from 600 nm to 1000 nm. The results show that the nano - particles of cuprous oxide samples are in a regular spherical shape, and the size is uniform and the dispersibility is good.
Key words: liquid phase synthesis, nano - cuprous oxide, organic additive
目录
目录 1
一、绪论 1
1.1课题背景 1
1.2 纳米材料概述 2
1.3.1氧化亚铜概述及合成研究 3
1.3.2不同形貌氧化亚铜的制备 4
1.4纳米氧化亚铜的表征分析 5
1.4.1 X射线衍射物相分析 5
1.5 纳米氧化亚铜的性能研究及应用 5
1.5.1 抗菌剂 5
二、 纳米氧化亚铜的制备与性能表征 5
2.1 实验试剂及仪器 6
2.1.1 主要试剂 6
2.1.2 实验仪器 6
2.2 纳米氧化亚铜制备工艺流程 7
2.2.1 以抗坏血酸作为添加剂的氧化亚铜的制备 7
2.2.2 以葡萄糖作为添加剂的纳米氧化亚铜的制备 8
2.3 纳米氧化亚铜的形貌表征 9
三、结果与分析 10
3.1 纳米氧化亚铜的形貌分析 10
3.1.1 以抗坏血酸作为添加剂的氧化亚铜的扫描电镜分析 10
3.1.2 以葡萄糖作为添加剂的纳米氧化亚铜的制备的扫描电镜分析 16
四、总结 21
致谢 22
参考文献 23
一、绪论
当今世界科技迅猛发展，尤其是结构材料的发展，大大推动了功能材料的应用。由于多维度微纳米材料的特殊结构和优异性能，在诸多领域有着广泛的应用，近年来多维度微纳米材料的研究引起了人们广泛关注，取得了引人注目的成就[1]。
近年来，在国内外学者的不断努力下，各种新颖的制备方法给人们带来的经济和社会效益已经初见成效。随着结晶学理论在实际生产应用中的实施，反馈关于纳米晶体制备工艺的信息，使得人们对结晶学理论有了更深入的研究，对晶体的微观结构与生长方式有了更深入的了解。人们逐渐掌握决定晶体材料性能的本质，并通过新的制备方法，制备出性能更加优异的新型材料。 规整形貌氧化亚铜的制备与性能研究:http://www.751com.cn/huaxue/lunwen_80127.html