摘要本论文通过选择具有柔性的V型多羧酸配体与稀土离子Ho3+和Nd3+进行溶剂热反应，成功制备出两例新颖的金属−有机框架结构Ho−HMDIA和Nd−HMDIA，通过X-射线单晶衍射进行了结构表征。虽然起始有机连接体都是采用V型H4MDIA (H4MDIA = 5,5′-亚甲基二间苯二甲酸) 配体且合成方法相同，但是两种晶体结构中配体的配位模式有着明显的不同，Ho离子是8配位的，并且Ho−HMDIA为单斜晶系，空间群为P2(1)/c。在Nd−HMDIA中，Nd(III)离子为9配位，Nd−HMDIA结晶于三斜晶系，其空间群为P-1。并且Ho−HMDIA和Nd−HMDIA这两个化合物的不对称单元组成不同，且两者在晶体堆积形式和孔道尺寸上也有明显的差异。并测试了上述化合物的红外和荧光光谱。69119
该论文有图9幅，表5个，参考文献13篇。
毕业论文关键词：金属−有机框架 金属结点 有机连接体 V型配体
The construction and structure study of MOFs based on V-shaped ligand
Abstract
In this paper, through solvothermal reaction of a V-shaped flexible tetracarboxylate linker and holmium/neodymium ions, two novelty lanthanide metal−organic frameworks, Ho−HMDIA and Nd−HMDIA have been synthesized and characterized by X-ray crystallography. Although the ligand is same, as well as the synthetic methods, the coordination models of the V-shaped ligand in Ho−HMDIA and Nd−HMDIA are different. In addition, the accumulation form and the size of porous of Ho−HMDIA and Nd−HMDIA are also different. The infrared spectroscopy and fluorescence spectroscopy were also performed for the above two MOFs and H4MDIA ligand.
Key words: Metal-organic frameworks (MOFs) Metal nods Organic linker V-shaped ligand
目 录
摘要Ⅰ
Abstract-Ⅱ
目录Ⅲ
图清单-Ⅳ
表清单-Ⅳ
1绪论1
1.2基于V型配体的稀土MOFs的概述1
2 实验2
2.1配体合成线路2
2.2实验仪器及试剂-2
2.3实验过程-3
3结果与讨论3
3.1化合物Ho−HMDIA的结构-4
3.2化合物Nd−HMDIA的结构-7
3.3配合物Ho−HMDIA和Nd−HMDIA的红外光谱表征-9
3.4配合物Ho−HMDIA和Nd−HMDIA的荧光光谱测试10
4 结论-10
参考文献11
致谢13
图清单
图序号 图名称 页码
图1-1 文献13所报道的相关晶体中金属的配位模式及荧光发射图 2
图2-1 本论文所涉及配体的合成路线 2
图3-1 化合物Ho−HMDIA的不对称单元结构图 4
图3-2 (a) 在Ho−HMDIA中Ho1离子中心的配位环境图；(b) 沿着b轴方向观察的Ho−HMDIA三维结构图 5
图3-3 化合物Nd−HMDIA的不对称单元结构图
6
图3-4 (a) 配合物Nd−HMDIA中Nd离子中心的配位环境图；(b) 双核Nd的结构图；(c)沿着c轴方向观察配合物Nd−HMDIA的三维结构图
（a)
（b) (b)双核Nd的结构图；(c) 沿着c轴方向观察配合物Nd−MDIA的三维结构 7
图3-5 基于V型配体稀土MOFs的构筑及其结构研究:http://www.751com.cn/huaxue/lunwen_77839.html