摘要：本文系统研究了磁场对管线钢X70在NS4溶液、格尔木土壤模拟液、大港土壤模拟液、大庆土壤模拟液和拉萨土壤模拟液等5种溶液中发生的电化学腐蚀的影响。通过分析有无磁场存在时的开路电位、电化学阻抗谱和塔菲尔曲线的变化情况，得出了；磁场能够促进管线钢X70在5种土壤模拟液中的电化学腐蚀，而且施加的磁场强度越强，电化学腐蚀就发生的越剧烈。51221

毕业论文关键词：磁场、管线钢X70、土壤环境、电化学腐蚀

Effects of Magnetic field on the electrochemical corrosion of pipeline steel in soil environment

Abstract: In this paper, effects of magnetic field on the electrochemical corrosion of X70 pipeline steel are studied systematically in NS4 solution, Golmud simulated soil solutions, Dagang simulated soil solutions, Daqing simulated soil solutions and Lhasa simulated soil solutions. With the presence of the magnetic field or not, the changes of the open circuit potential, the electrochemical impedance spectra and the Tafel plots are analyzed. The experiments results showed that the magnetic field could promote the electrochemical corrosion of X70 steel; and the stronger the magnetic field is, the more intense the electrochemical corrosion is.

Keywords: magnetic field, X70 steel, soil environment, electrochemical corrosion

1.  前言

随着我国石油天然气管道的不断建设和城市化进程的加快,石油天然气管道不可避免地受到电力设施及高压线所产生的磁场的影响。关于磁场对管线钢腐蚀的研究，目前还不是很多。有资料[1] 报道外加小磁场能够减缓金属的腐蚀，而大磁场却会加速腐蚀，腐蚀速率与磁场强度存在着一定关系。谢发勤等[2] 研究了磁场对20号钢在模拟污水介质中腐蚀行为产生的影响，发现磁场对电极表面Fe3O4的生成有促进作用、能够使得开路电位正移。

中国西气东输一线工程采用的是管线钢X70，因此研究磁场对管线钢X70在各种土壤环境中的腐蚀产生的影响具有重要的实际应用价值。

本文研究磁场对管线钢X70在NS4溶液、格尔木土壤模拟液、大港土壤模拟液、大庆土壤模拟液和拉萨土壤模拟液等5种溶液中的电化学腐蚀产生的影响。外加不同磁场情况下，通过电化学分析分析开路电位、电化学阻抗谱和塔菲尔曲线的变化，研究磁场对管线钢X70在土壤环境中电化学腐蚀行为的影响。

2. 实验部分

2.1实验材料及溶液

本实验使用的工作电极由国产管线钢X70制成，X70 钢的化学成分（质量分数，%）为：C 0.055、Si 0.220、Mn 1.620、P 0.013、S 0.002、Ti 0.019、V 0.001、Nb 0.110、Fe 余量。

表 1.5种土壤模拟溶液的化学成分

模拟土壤 质量浓度 c/(g•L-1)

NaCl CaCl2 Na2SO4 MgSO4•7H2O NaHCO3 KNO3 MgCl4•6H2O

格尔木 56.631 10.489 11.928 -- 0.474 0.980 35.169

大港站 25.020 1.049 0 5.227 0.249 0.306 --

大庆站 0 磁场对管线钢在土壤环境中发生的电化学腐蚀的影响:http://www.751com.cn/huaxue/lunwen_54781.html