摘要: 离子交换树脂有广泛的应用和广阔的发展前景。本文是通过悬浮聚合的方法，以甲基丙烯酸甲酯与二乙烯苯共聚合成聚甲基丙烯酸甲酯树脂珠。然后以三乙烯四胺（TETA）为胺化剂，采用不同溶剂，得到新型胺化树脂珠，并且对胺化前后的树脂珠进行功能基含量的测试和红外表征，分析获得胺化树脂最适合的溶剂。并通过紫外测试分析其吸附和解吸能力。41395
毕业论文关键词：离子交换树脂；甲基丙烯酸甲酯；胺化；吸附
New preparation method of polypropylene acid type anion exchange resin
Abstract: Ion exchange resins have a wide range of applications and broad prospects for development. In this paper, we use the method of suspension polymerization to synthesize poly methyl methacrylate resin beads by copolymerization of methyl methacrylate and pinyl-benzene. Then with triethylenetetramine (TETA) as aminating agent and different solvents, novel aminated resin beads, and before and after the aminated resin beads of functional group content of test and FTIR, obtained from the analysis of amine resin was the most suitable solvent. And the adsorption and desorption capacity were analyzed by UV test.
Keyword: ion exchange resin；methyl methacrylate；amination；adsorption
目  录
1    绪论    1
1.1    离子交换树脂综述    1
1.1.1    离子交换树脂简介    1
1.1.2    离子交换作用原理    1
1.1.3    离子交换树脂的分类    2
1.1.4    离子交换树脂功能    3
1.1.5    离子交换树脂的应用    4
1.2    聚丙烯酸型离子交换树脂    5
1.2.1    聚丙烯酸型离子交换树脂概述    5
1.2.2    聚丙烯酸型离子交换树脂合成方法    6
1.3    主要的除磷技术    6
1.3.1    化学沉淀法    7
1.3.2    吸附法    7
1.3.3    电渗析法    7
1.3.4    离子交换法    7
1.3.5    结晶法    7
1.4    课题主要研究背景和意义    8
1.5    方案论证    8
2    实验部分    9
2.1    实验原料与设备    9
2.1.1    实验原料    9
2.1.2    实验仪器    9
2.2    树脂的制备    10
2.2.1    MMA的处理    10
2.2.2    PMMA的合成    10
2.2.3    树脂的胺化    11
2.3    树脂的测试及表征    12
2.3.1    功能基含量的测定    12
2.3.2    红外图谱表征    12
2.3.3    紫外分光光度计的测定    13
3    结果与讨论    15
3.1    溶剂对树脂功能基含量的影响    15
3.2    树脂红外分析    15
3.3    紫外分析    16
4    结论    21
致  谢    22
参考文献    23

1    绪论
1.1    离子交换树脂综述
1.1.1    离子交换树脂简介 聚丙烯酸型阴离子交换树脂的新制备方法:http://www.751com.cn/huaxue/lunwen_41446.html